tailieunhanh - Tính chất của vật liệu apatite với titan dioxit pha tạp nitơ ứng dụng loại bỏ một số hợp chất hữu cơ ở không khí trong nhà

Mục đích của nghiên cứu này là đưa ra một số tính chất của TiO2 pha tạp nitơ được phủ apatit (Ap/N-TiO2) có hoạt tính quang xúc tác tốt trong vùng ánh sáng khả kiến và ứng dụng để loại bỏ khí formaldehyde trong không khí trong nhà. | TNU Journal of Science and Technology 228 14 106 - 113 PROPERTIES OF APATITE WITH NITROGEN-DOPED TITANIUM DIOXIDE APPLIED TO REMOVE SOME ORGANIC COMPOUNDS FROM INDOOR AIR Nguyen Thi Hue1 4 Nguyen Ha Giang1 Chu Viet Hai1 Nguyen Xuan Dat1 Khuc Nang Hieu2 Nguyen Thi Thu Thuy3 1 Institute of Environmental Technology VAST 2Son La Pedagogical College 3 TNU - University of Science 4Graduate University of Science and Technology - VAST ARTICLE INFO ABSTRACT Received 17 8 2023 The purpose of this study is to present some properties of apatite-coated nitrogen-doped TiO2 Ap N-TiO2 with good photocatalytic activity in the Revised 17 10 2023 visible light region and apply it to remove formaldehyde gas in indoor air. Published 18 10 2023 The morphology elemental composition ratio as well as the surface area and average pore size of the materials were confirmed by SEM EDX and BET respectively. N is dopped in the crystal of TiO 2 at a different molar KEYWORDS ratios the results showed that with a ratio of 2 1 N TiO2 the mass percent Apatite of N that was injected into the TiO2 crystal is the highest and the doping is the best compared to the remaining samples. In the visible light region 365 TiO2 nm 20 W the N-doped Ap TiO2 sample has better photocatalytic activity Ap N-TiO2 than the undoped sample. Methylene blue solution with an initial Formaldehyde concentration of 20 ppm was completely reduced after 120 minutes of illumination while Formaldehyde at a concentration of 8 ppm the Methylene blue treatment efficiency was only 78 after 26 hours. After treatment the concentration of Formaldehyde reached the permissible standard QCVN 06 2009 BTNMT. Ap N-TiO2 materials will have great promise in reducing pollution by other harmful chemicals in the air environment. TÍNH CHẤT CỦA VẬT LIỆU APATITE VỚI TITAN DIOXIT PHA TẠP NITƠ ỨNG DỤNG LOẠI BỎ MỘT SỐ HỢP CHẤT HỮU CƠ Ở KHÔNG KHÍ TRONG NHÀ Nguyễn Thị Huệ1 4 Nguyễn Hà Giang1 Chu Việt Hải1 Nguyễn Xuân Đạt1 Khúc Năng Hiệu2 Nguyễn Thị Thu Thúy3