tailieunhanh - Khảo sát ảnh hưởng độ pH của methyl đỏ hấp phụ trên tấm vuông nano bạc lên phổ tán xạ raman tăng cường bề mặt

Bài viết Khảo sát ảnh hưởng độ pH của methyl đỏ hấp phụ trên tấm vuông nano bạc lên phổ tán xạ raman tăng cường bề mặt giới thiệu kết quả khảo sát ảnh hưởng của độ pH của MR lên phổ tán xạ Raman tăng cường bề mặt (SERS) khi chúng hấp phụ trên đế nano bạc dạng cầu (Ag-NPs) và dạng tấm vuông (Ag-PS). | TNU Journal of Science and Technology 228 02 327 - 334 INVESTIGATION OF THE pH EFFECT OF METHYL RED ADSORBED ON SILVER NANO PLATE SQUARE TO SURFACE ENHANCED RAMAN SCATTERING Pham Thi Thu Ha1 Nguyen Thi Loan1 2 Vu Xuan Hoa1 1 TNU- University of Sciences 2Pham Kinh An Secondary School Thai Binh province ARTICLE INFO ABSTRACT Received 16 01 2023 In this study we present the results of investigating the pH effect of methyl red MR on surface-enhanced Raman spectroscopy SERS Revised 27 02 2023 using the substrate of the silver nanoparticles Ag-NPs and silver Published 28 02 2023 plates square Ag-PS . Ag-PS were fabricated by photochemical method under green light-emitting diode LED irradiation λ 532 nm onto a solution of silver nanoparticles. Morphology and size of the KEYWORDS as-obtained Ag-PS were characterized by scanning electron microscopy Silver nanoparticles SEM and transmition electron microscopy TEM . Optical properties were characterized by ultraviolet- visible absorption. The crystal Methyl red structure of the samples was investigated by X-ray diffraction XRD . pH Surface-enhanced Raman scattering spectroscopy SERS was used to Surface enhanced Raman investigate the effect of pH and . The results scattering show that when pH lt 5 the Raman spectral intensity is strongly LED enhanced at 1609 cm-1 while at pH gt 5 it is enhanced at 1396 cm-1. Interestingly at pH the linear dependence between the logarithm of the SERS signal intensity log I and the logarithm of the MR concentration log C occurred in the range from 3 10 -8 M to 10-4 M and detection of limit LOD reach 3 10-8 M. KHẢO SÁT ẢNH HƯỞNG ĐỘ pH CỦA METHYL ĐỎ HẤP PHỤ TRÊN TẤM VUÔNG NANO BẠC LÊN PHỔ TÁN XẠ RAMAN TĂNG CƯỜNG BỀ MẶT Phạm Thị Thu Hà1 Nguyễn Thị Loan1 2 Vũ Xuân Hoà1 1 Trường Đại học Khoa học- ĐH Thái Nguyên 2Trường Trung học cơ sở Phạm Kính Ân tỉnh Thái Bình THÔNG TIN BÀI BÁO TÓM TẮT Ngày nhận bài 16 01 2023 Trong nghiên cứu này chúng tôi giới thiệu kết quả khảo sát .