High flame retardant performance of SiO2-TiO2 sol coated on polyester/cotton fabrics

Đang chuẩn bị nút TẢI XUỐNG, xin hãy chờ

SiO2 and TiO2 sols were successfully synthesized by using sodium silicate and titanium chloride as Si and Ti sources. SiO2-TiO2 sol coated polyester/cotton fabric was fabricated by deepcoating method and using SiO2 , TiO2 sols as coating materials. SiO2 -TiO2 coated fabric were characterized by XRD, FTIR, TGA, SEM and EDX. From SEM image, it showed the SiO2, TiO2 particles of 20-30 nm which well deposited on fabric surface. TGA result revealed the significant improvement of thermal resistance and stability of SiO2-TiO2 coated fabric as compared to those of uncoated fabric. |

TÀI LIỆU LIÊN QUAN

Mechanical properties and flame resistance of composite based on high density polyethylene/ethylene vinyl acetate blend and novel organically modified waste gypsum

Novel flame retardant poly(thiourea-sulfone-imide)s for high temperature applications: synthesis and characterization

High flame retardant performance of SiO2-TiO2 sol coated on polyester/cotton fabrics

High temperature Air Combustion From Energy Conservation to Pollution Reduction

báo cáo khoa học: " Patients presenting with miliaria while wearing flame resistant clothing in high ambient temperatures: a case series"