Influence of substitution of the magnetic 3d metals FOR Mn in perovskite La0.67Ca0.33Mn0.90TM0.10O3 (TM = Fe, Co, Ni) compounds

Influence of substitution of 3d metals for Mn on properties of La0.67Ca0.33Mn0.9 TM0.1O3 (TM = Fe, Co, Ni) compounds was studied. Ferromagnetic – paramagnetic and metals – insulator transitions were significantly affected by Mn-site substitution. However, no observable difference was found in their crystal structure from X-ray diffraction analysis. At room temperature the structure characterization of these compounds gave the single phase and structure is the distortion orthorhombic cell with space group symmetry Pnma. The magnetoresistance measurement showed that the magnetoresistance ratio MR increases until 17% in magnetic field of 0.4 T, and in low magnetic field region (µoH | Influence of substitution of the magnetic 3d metals FOR Mn in perovskite La0.67Ca0.33Mn0.90TM0.10O3 TM Fe Co Ni compounds