tailieunhanh - Phân tách hỗn hợp cồn-nước bằng quá trình hấp phụ trên ray phân tử zeolit 3A để xác định cồn nhiên liệu

5A, 4A and 3A zeolites were successfully prepared using solid seeds at pilot scale. The adsorption properties of 5A, 4A and 3A zeolites were determined by adsorption isotherm method. The results showed that water adsorption capacity and rate of 5A and 4A zeolites were higher than those of 3A zeolite. Even at low vapor pressure of water of 4 mmHg, adsorption capacity of 5A, 4A and 3A zeolites also reached about 23%, 22% and 17%, respectively, and was much higher than that of silicagel (5%). Especially, 3A zeolite exhibited a good selectivity to water molecule, so it was used as an excellent adsorbent to remove selectively water from ethanol-water mixture for the production of ethanol fuel. Liquid phase separation of ethanol-water mixture by adsorption on 3A zeolite was also investigated. The results indicated that the adsorption equilibrium was achieved around 1 hour. In order to obtain absolute ethanol ( ), the required 3A zeolite amount was times higher than that of theoretical calculation. | Tạp chí Hóa học T. 45 6A Tr. 88 - 92 2007 PHÂN TÁCH HỖN HỢP CỒN-NƯỚC BẰNG QUÁ TRÌNH HẤP PHỤ TRÊN RÂY PHÂN TỬ ZEOLIT 3A ĐỂ sản xuất CỒN NHIÊN LIỆU Đến Tòa soạn 15-11-2007 ĐẶNG TUYẾT PHƯƠNG HOÀNG YẾN TRAN QUANG VINH ĐINH CAO THẮNG BÙI HẢI LINH TRAN THỊ KIM HOA HOÀNG VINH THÂNG VŨ ANH TUẤN Viện Hóa học Viện Khoa học vá Công nghệ Việt Nam SUMMARY 5A 4A and 3A zeolites were successfully prepared using solid seeds at pilot scale. The adsorption properties of 5A 4A and 3A zeolites were determined by adsorption isotherm method. The results showed that water adsorption capacity and rate of 5A and 4A zeolites were higher than those of 3A zeolite. Even at low vapor pressure of water of 4 mmHg adsorption capacity of 5A 4A and 3A zeolites also reached about 23 22 and 17 respectively and was much higher than that of silicagel 5 . Especially 3A zeolite exhibited a good selectivity to water molecule so it was used as an excellent adsorbent to remove selectively water from ethanol-water mixture for the production of ethanol fuel. Liquid phase separation of ethanol-water mixture by adsorption on 3A zeolite was also investigated. The results indicated that the adsorption equilibrium was achieved around 1 hour. In order to obtain absolute ethanol the required 3A zeolite amount was times higher than that of theoretical calculation. I - MỞ ĐAU Cồn rượu etylic etanol là một loại hoá chất có nhiều ứng dụng trong công nghiệp cũng như dân sinh như làm dung môi chất tẩy trùng. Đặc biệt là nửa sau thế kỷ XX đến nay kể từ khi cuộc khủng hoảng dầu mỏ vào thập niên 70 của thế kỷ trước bùng nổ giá dầu mỏ liên tục tăng và có nguy cơ cạn kiệt trong vòng vài chục năm tới thì ethanol được xem như là một ứng cử viên sáng giá có thể thay thế xăng từ nguồn dầu mỏ. Đây là nguồn năng lượng sạch thân thiện với môi trường và có thể tái tạo được 1-3 . Hiện nay nhiều nước trên thế giới đã và đang dùng cồn pha trộn vào xăng làm nhiên liệu cho động cơ ô tô xe máy nhằm tăng trị số octan và giảm khí thải