The photo catalytic efficiency of some TiO2 films (TiO2-ST01; TiO2-P25; TiO2 sol-gel) immobilized on glass has been investigated for the degradation of phenol in aqueous solution under UV light. It was shown that the best result obtained with TiO2-ST01 film, where the mineralization was the highest (70% TOC was removed after 3 hours of irradiations) and that related to the smaller particle size and the bigger surface areas of the TiO2-ST01 particles compared with TiO2-P25 and TiO2 sol-gel films. The effect of pH and phenol concentration were discussed. The kinetics of reaction is described by Langmuir-Hinshelwood model and pseudo- first-order for the low ranges of phenol < 70 mg/l. The highest degradation yield was obtained at pH neutral with the removal of TOC up to 70% after 3 hours of reaction. | 1 Tạp chí Hóa học T. 42 3 Tr. 265 - 270 2004 PHÂN HỦY PHENOL TRÊN MÀNG TiO2 VỚI ÁNH SÁNG TỬ NGOẠI-UV Đến Tòa soạn 16-7-2003 NGUyỄN THỊ DUNG1 PHẠM PHÁT TÂN1 NGUyỄN VÃN KHQA1 TRẦN THỊ Đức2 LÊ THỊ HQÀINAM3 BÙI TIÊN DŨNG3 Viện Công nghệ Hóa học Viện Khoa học vá Công nghệ Việt Nam 2Viện Vật lý ứng dụng vá Thiết bị khoa học Viện Khoa học vá Công nghệ Việt Nam 3Viện Hóa học Viện Khoa học vá Công nghệ Việt Nam SUMMARY The photo catalytic efficiency of some TiO2 films TiO2-ST01 TiO2-P25 TiO2 sol-gel immobilized on glass has been investigated for the degradation of phenol in aqueous solution under UV light. It was shown that the best result obtained with TiO2-ST01 film where the mineralization was the highest 70 TOC was removed after 3 hours of irradiations and that related to the smaller particle size and the bigger surface areas of the TiO2-ST01 particles compared with TiO2-P25 and TiO2 sol-gel films. The effect of pH and phenol concentration were discussed. The kinetics of reaction is described by Langmuir-Hinshelwood model and pseudo-first-order for the low ranges of phenol 70 mg l. The highest degradation yield was obtained at pH neutral with the removal of TOC up to 70 after 3 hours of reaction. I - MỞ ĐẦU Những năm gần đây vấn đề ô nhiễm môi trường do chất thải của các ngành sản xuất ngày càng nghiêm trọng đòi hỏi các nhà khoa học và công nghệ phải nghiên cứu những phương pháp có hiệu quả để xử lý các chất ô nhiễm hữu cơ trong nước. Một trong những phương pháp có triển vọng là phương pháp oxi hóa nâng cao AOP trong đó có sử dụng các chất xúc tác dị thể bán dẫn TiO2 ZnO CdS SnO. Những công trình nghiên cứu tổng quan của Schiavello 1988 Serpone và đổng tác giả 1989 Ollis và đổng tác giả 1993 Hernmann và đổng tác giả 1993 1 - 4 đã chỉ ra rằng bản chất của xúc tác quang là ở chỗ khi chất bán dẫn được chiếu chùm tia photon có năng lượng bằng hoặc cao hơn năng lượng vùng trống EG hv Eg thì năng lượng này đủ bứt một electron từ vùng hóa trị lên vùng dẫn và kết quả tạo ra một