In 1998, it was first reported that a silica material with large, uniform mesopores arranged into a two-demensional hexagonal structure is synthesized using triblock copolymer and oligomer templates poly (ethylene oxide), (EO)n. This silica was denoted SBA-15. Up to now, it is believed that ordered mesopores of SBA-15 are connected through complementary pores (microporores and small mesopores) in the siliceous pore walls. SBA-15 can be readily synthesized using cheap materials and it shows attractive structural properties, very good hydrothemal stability. SBA-15 can be used as adsorbents, large pore ordered mesoporous catalysts after having implanted heteratomes in its framework. In this report, a series of SBA-15 was synthesized and studied their structural characteristics depending on synthese temperature by modern physical methods: XRD, nitrogen adsorption-desorption isotherms and HR-TEM. | Tạp chí Hóa học T. 44 3 Tr. 317 - 321 2006 NGHIÊN cứu TỔNG HỢP BIÊN TÍNH VÀ ĐẶC TRƯNG VẬT LIỆU SILICA MAO QUẢN TRUNG BÌNH SBA-15 LÀM xúc Tác CHUYỂN HÓA CÁC HỢP CHẤT THƠM PHẨN I - NGHIÊN CỨU TỔNG HỢP VÀ ĐẶC TRƯNG VẬT LIỆU SILICA MAO QUẢN tRuNG bình SBA-15 Đến Tòa soạn 29-6-2005 VŨ THÀNH NAM HQA Hữu THU OTGQN-UUL ENKH-UyANGA Khoa Hóa học Trường ĐHKHTN - ĐHQG Hà Nội SUMMARy In 1998 it was first reported that a silica material with large uniform mesopores arranged into a two-demensional hexagonal structure is synthesized using triblock copolymer and oligomer templates poly ethylene oxide EO n. This silica was denoted SBA-15. Up to now it is believed that ordered mesopores of SBA-15 are connected through complementary pores microporores and small mesopores in the siliceous pore walls. SBA-15 can be readily synthesized using cheap materials and it shows attractive structural properties very good hydrothemal stability. SBA-15 can be used as adsorbents large pore ordered mesoporous catalysts after having implanted heteratomes in its framework. In this report a series of SBA-15 was synthesized and studied their structural characteristics depending on synthese temperature by modern physical methods XRD nitrogen adsorption-desorption isotherms and HR-TEM. I - MỞ ĐẦU SBA-15 là loại vật liệu silica có lỗ xốp đổng đều rộng được sắp xếp thành cấu trúc lục lăng hai chiều. Vật liệu này có diện tích bề mặt riêng lớn từ 700 đến 900 m2 g cỡ lỗ rộng từ 5 đến 9 nm và thành lỗ dày từ 3 5 đến 5 3 nm 2 . Đầu tiên người ta cho rằng các lỗ của vật liệu silica SBA-15 giống như các ống hình lục lăng không nố i với nhau. Tuy nhiên những công trình nghiên cứu sao chép bằng cacbon và platin 3 4 đã cho thấy các lỗ trung bình trật tự của SBA-15 được nối với nhau qua các hệ thống lỗ phụ là vi lỗ và lỗ trung bình micropores and mesopores trong thành của các lỗ xốp 6 . Có tác giả 5 cho rằng các lỗ phụ được hình thành liên quan đến chất tạo cấu trúc có trong thành của các ống silica trong quá trình .

crossorigin="anonymous">
Đã phát hiện trình chặn quảng cáo AdBlock
Trang web này phụ thuộc vào doanh thu từ số lần hiển thị quảng cáo để tồn tại. Vui lòng tắt trình chặn quảng cáo của bạn hoặc tạm dừng tính năng chặn quảng cáo cho trang web này.