tailieunhanh - Nghiên cứu độ bền thời tiết và khả năng ứng dụng của vật liệu nanocompozit pvc/dop/clay

Bài báo trình bày kết quả nghiên cứu độ bền thời tiết và khả năng ứng dụng của vật liệu compozit chế tạo từ PVC v à clay biến tính của Việt Nam. | Tạp chí Hóa học T. 45 ĐB Tr. 66 - 72 2007 NGHIÊN cứu ĐỘ BỂN THỜI TIET VÀ KHẢ NĂNG ỨNG DỤNG CỦA VẬT LIỆU NANOCOMPOZIT PVC DOP CLAY Đến Tòa soạn 15-11-2007 THÁI HQÀNG1 NGUyỄN THẠC KIM1 Đỗ QUANG THAM1 NGưyEN THỊ KIM DUNG1 LỮÁNH NGỌC2 1Viện Kỳ thuật nhiệt đới Viện Khoa học vá Công nghệ Việt Nam 2Khoa Hóa học Trường Đại học Sư phạm Há Nội SUMMARY Poly vinyl chloride PVC ldioctyl phthalate DOP lorganoclay nanocomposites with varied amounts of organoclay and DOP were prepared by melt intercalation. The weather endurance of the composites was examined on weathering test chamber UV CON NC 327-2. The tensile strength and elongation at break of the materials were determined with tensile tester WPM and their thermo-oxidative resistance was evaluated after testing the samples at 100oC for 72 hours. The flame retardancy of the materials was measured by UL-94 vertical method and their solvent resistance was determined by immersing the samples in toluene - acetone mixture at room temperature for 168 hours. The electrical parameters of the composites were measured by the dielectric loss measuring set TR-10C according to ASTM D150 and D149. The obtained results show that the weather endurance of the materials with a small amount of organoclay is higher than that of the materials without organoclay and reaches maximal values at 2 wt organoclay content. Generally the flame retardancy and solvent resistance of the composites containing organoclay are dramatically improved. Specially the composites containing 1 wt organoclay and 30 35 wt DOP have the best flame retardancy as well as solvent resistance. By comparison the electrical and mechanico-physical properties as well as thermooxidative resistance of PVClDOPlclay nanocomposites with those of some commercial PVC materials using in electrical industry it revealed that the nanocomposites containing 1 wt organoclay and 30 35 wt DOP well meet requirements of insolation materials. I - MỞ ĐẦU Poly vinyl clorua PVC là một trong