tailieunhanh - Nghiên cứu khả năng ức chế ăn mòn thép trong dung dịch Nacl 0,1 M của Clay hữu cơ nanofil5

Corrosion inhibition of organic clay nanofil5 in NaCl M solution was studied by polarization curves and electrochemical impedance spectroscopy. The clay concentrations studied were between 1 g/l and 5 g/l. The clay nanofil5 plays both anodic and cathodic corrosion inhibition. The corrosion inhibition of clay nanofil5 depends on the concentration. The results obtained by two methods were in good agreement and showed that the highest inhibition efficiency was obtained with the nanofil5 concentration of 3 g/l. The influence of the immersion time on the inhibition efficiency was also studied. The results indicated that at the first 120 minutes of immersion the inhibition efficiency increased rapidly, which was about . Then the inhibition efficiency did not changed very much with immersion time, after 240 minutes of immersion the inhibition efficiency was . Surface anlyse by SEM indicated the presence of clay platelets on steel surface after immersion in NaCl M solution containing 3 g/l nanofil5. | Tạp chí Hóa học T. 44 6 Tr. 739 - 744 2006 NGHIÊN CỨU KHẢ NĂNG ỨC CHE ĂN MÒN THÉP TRONG DUNG DỊCH NaCl 0 1 M CỦA CLAY HỮU Cơ NANOFIL5 Đến Tòa soạn 16-2-2006 TÔ THỊ XUÂN HẰNG1 NGUyỄN THỊ THE LOAN2 PHẠM GIA VŨ1 TRỊNH ANH TRÚC1 1Viện kỳ thuật Nhiệt đới Viện Khoa học vá Công nghệ Việt Nam 2Trường Đại học khoa học tự nhiên Thánh phố Hồ Chí Minh SUMMARy Corrosion inhibition of organic clay nanofil5 in NaCl M solution was studied by polarization curves and electrochemical impedance spectroscopy. The clay concentrations studied were between 1 g l and 5 g l. The clay nanofil5 plays both anodic and cathodic corrosion inhibition. The corrosion inhibition of clay nanofil5 depends on the concentration. The results obtained by two methods were in good agreement and showed that the highest inhibition efficiency was obtained with the nanofil5 concentration of 3 g l. The influence of the immersion time on the inhibition efficiency was also studied. The results indicated that at the first 120 minutes of immersion the inhibition efficiency increased rapidly which was about . Then the inhibition efficiency did not changed very much with immersion time after 240 minutes of immersion the inhibition efficiency was . Surface anlyse by SEM indicated the presence of clay platelets on steel surface after immersion in NaCl M solution containing 3 g l nanofil5. I - MỞ ĐẦU Đã từ lâu clay dạng bentonit đã được sử dụng làm bột độn cũng như phụ gia trong polyme và lớp phủ. Trong những năm gần đây công nghệ nano đã tạo ra các loại vật liệu nanocompozit với các tính năng kỹ thuật nổi trội mà vật liệu thông thường không có 1 - 4 . Clay hữu cơ được sử dụng ngày càng nhiều trong các vật liệu nanocomopozit đặc biệt trong lớp phủ nanocompozit 5 - 9 . Chỉ với nồng độ nanoclay hữu cơ rất nhỏ đã tăng khả năng bảo vệ của màng sơn lên rất nhiều. Nhiều công trình công bố cho thấy pigment trao đổi ion trên cơ sở clay bentonit có khả năng ức chế ăn mòn cao có thể thay thế cromat là pigment có .