tailieunhanh - Ảnh hưởng của hoá già đến sức kháng nứt của hỗn hợp bê tông asphalt tái chế ấm có tỷ lệ RAP cao

Bài viết Ảnh hưởng của hoá già đến sức kháng nứt của hỗn hợp bê tông asphalt tái chế ấm có tỷ lệ RAP cao trình bày kết quả nghiên cứu thực nghiệm đánh giá sức kháng nứt của hỗn hợp bê tông asphalt tái chế ấm có tỷ lệ RAP bằng 30% và 50%. | Transport and Communications Science Journal Vol 72 Issue 8 10 2021 920-931 Transport and Communications Science Journal THE EFFECT OF AGING ON THE CRACKING RESISTANCE OF WARM MIX ASPHALT WITH HIGH RAP CONTENT Nguyen Ngoc Lan Truong Van Quyet University of Transport and Communications No 3 Cau Giay Street Hanoi Vietnam. ARTICLE INFO TYPE Research Article Received 27 08 2021 Revised 28 09 2021 Accepted 06 10 2021 Published online 15 10 2021 https Corresponding author Email Tel 84978452140 Abstract. Asphalt mixtures containing Reclaimed Asphalt Pavement RAP have high stiffness due to the aged binder in these recycled materials. The evaluation of the cracking resistance of the asphalt mixture containing RAP is therefore a priority for the asphalt materials especially with high RAP content. In addition aging in asphalt binders is recognized as one of the factors causing cracking-related failures. Asphalt aging occurs during the production construction and service life of the pavements. Therefore the evaluation of asphalt mixtures cracking resistance is one of the critical items to assess the quality and durability of the pavements during the exploitation period. This paper presents the results of the evaluation of cracking resistance of warm mix asphalt with RAP contents of 30 and 50 under the different aging conditions. The IDEAL-CT determines cracking resistance through a fracture mechanics-based parameter Cracking Tolerance Index CTIndex . Three aging conditions were performed including the loose mixture including short-term oven aging at 135oC for 4 hours long-term oven aging at 135oC for 24 hours and long-term oven aging at 95oC for 8 days after short-term oven aging. Laboratory test results of the CTIndex indicated the influence of different aging conditions on the cracking resistance of warm mix asphalt with high RAP content. Keywords Warm mix asphalt Reclaimed asphalt pavement Recycled asphalt Aging Cracking .

• Kiến trúc - Xây dựng
• Hỗn hợp asphalt ấm
• Vật liệu cào bóc mặt đường asphalt cũ
• Asphalt tái chế
• Hoá già
• Sức kháng nứt
• Chỉ số kháng nứt
• Vật liệu asphalt tái chế
• Chất tái sinh Prephalt
• Độ lún vệt hằn bánh xe
• Chỉ số kháng nứt
• Bê tông asphalt
• Nhiệt độ bảo dưỡng
• Nhũ tương bitum
• Tái chế nguội
• Năng lượng phá huỷ
• Cường độ chịu kéo