tailieunhanh - Applied studies on material of Biocomposite biological origin prepared from oxide nano and biogum (extracted from Osaka seeds) for the treatment of methylene blue

Researching on Methyllen Blue dye treatment ability with Nano material (CoFe2O4 synthesized by co-precipitation method) combined with Biogum (extracted from Osaka Seeds (Cassia Fistula Linn). Research results show that with Biogum base material fully covered by magnetic nanoparticles of size 70-95 nm (SEM) and the presence of several specific functional groups for biogum and ferromagnetic oxide nano (FT-IR). When adding OH group to nano material, the adhestive ability to biogum and the size of the particle does not change. Results of comparative studies on the application of Nano-Biogum and Nano-OH-Biogum materials showed that when studying the dyeing color of Methylene blue, the treatment efficiency is from to , decreasing from Pt-Co. Pt-Co at pH 6-7 and dosage at g/l. Based on the above results, Nano - Biogum is able to treat dyeing color better than Nano OH - Biogum. Therefore, Nano - Biogum can become suitable material for the application of color treatment in practice. | Applied studies on material of Biocomposite biological origin prepared from oxide nano and biogum (extracted from Osaka seeds) for the treatment of methylene blue

• Sinh học
• Color treatment
• Materials of biological origin
• Methylene blue
• Treatment effiency
• Nano Biogum and Nano OH Biogum materials