tailieunhanh - Some properties of eucalyptus wood flour filled recycled high density polyethylene polymer composites

The mechanical properties of eucalyptus wood flours (EWF) filled recycled high density polyethylene (HDPE) composites were investigated. First thermal gravimetric analysis (TGA) and differential scanning calorimetry (DSC) analysis were conducted for recycled HDPE and EWF. | Turk J Agric For 32 (2008) 537-546 © TÜBİTAK Some Properties of Eucalyptus Wood Flour Filled Recycled High Density Polyethylene Polymer-Composites Fatih MENGELOĞLU*, Kadir KARAKUŞ Department of Forest Industry Engineering, Faculty of Forestry, Kahramanmaraş Sütçü İmam University, Kahramanmaraş - TURKEY Received: Abstract: The mechanical properties of eucalyptus wood flours (EWF) filled recycled high density polyethylene (HDPE) composites were investigated. First thermal gravimetric analysis (TGA) and differential scanning calorimetry (DSC) analysis were conducted for recycled HDPE and EWF. Later the effects of EWF and maleic anhydride grafted polyethylene (MAPE) concentrations were studied. TGA analysis revealed that EWF and recycled HDPE started degrading around 230 °C and 280 °C, respectively. Melting temperature of the recycled HDPE was around 129 °C. Mechanical property evaluation showed that the increased concentration of EWF in polymer-composites reduced the tensile, flexural, and impact strength while increased the tensile and flexural modulus. The addition of small amount of MAPE coupling agent improved the tensile and flexural strength but this increase was leveled off at higher concentrations. Impact strength of the composites was reduced by the coupling agent. This study showed that polymer-composites can be manufactured utilizing recycled HDPE and eucalyptus wood flours in the process temperature range of 130-230 °C and could provide additional income for the lumber mills and promote the recycling of HDPE. Key Words: Recycled HDPE, polymer-composites, mechanical properties, coupling agent, TGA, DSC Dolgu Maddesi Olarak Okaliptüs Unları Kullanılan Geri Dönüşüm Yüksek Yoğunluklu Polietilen Polimer-Kompozitlerin Bazı Özellikleri Özet: Bu çalışmada, okaliptüs odun unları (OOU) ve geri dönüşüm halindeki yüksek yoğunluklu polietilen (YYPE) kullanılarak üretilen polimer-kompozitlerin mekanik özellikleri araştırılmıştır. Öncelikli olarak, OOU ve

• Nông nghiệp
• Recycled HDPE
• Polymer composites
• Mechanical properties
• Coupling agent
• Differential scanning calorimetry
• Thermal gravimetric analysis
• Introduction to Thermal Analysis Methods
• Thermal Analysis used
• Thermal Analysis
• Differential Thermal Analysis
• Dynamic mechanics
• Thermal analysis measurements
• Thermo gravimetric analysis
• Polymeric materials
• Green method
• Graphene oxide
• Reduced graphene oxide
• Gas sensor
• Advanced materials and devices