tailieunhanh - Magnetic resonance imaging (MRI) application of Fe3O4 based ferrofluid synthesized by thermal decomposition using poly (maleic anhydride-alt-1-octadecene) ((PMAO)

The MRI image was detected with higher contrast in comparison with that before injecting. By comparing with the MRI images taken in T1 weighted the T2 weighted images are clearer. The MRI images of a rabbit taken by the T2 weighted which shows that our coated ferrite nanoparticles can be used as a T2 MRI contrast agent. | Vietnam Journal of Science and Technology 56 (1A) (2018) 174-182 MAGNETIC RESONANCE IMAGING (MRI) APPLICATION OF Fe3O4 BASED FERROFLUID SYNTHESIZED BY THERMAL DECOMPOSITION USING POLY (MALEIC ANHYDRIDE -ALT-1OCTADECENE) (PMAO) Le The Tam1, *, Vuong Thi Kim Oanh2, Nguyen Hoa Du1, Le Trong Lu3, Nguyen Thi Hai Hoa5, Le Ngoc Tu6, Tran Dai Lam4, * 1 Vinh University, 182 Le Duan, Vinh City, Vietnam. 2 Institute of Materials Science, VAST, 18 Hoang Quoc Viet Road, Ha Noi 3 Institute for Tropical Technology, VAST, 18 Hoang Quoc Viet Road, Ha Noi 4 Graduate University of Science and Technology, VAST, 18 Hoang Quoc Viet Road, Ha Noi 5 University of Science and Technology of Hanoi, VAST, 18 Hoang Quoc Viet Road, Ha Noi 6 National Psychiatric Hospital No1– Thuong Tin, Ha Noi * Email: tamlt@, tdlam@ Received: 15 August 2017; Accepted for publication: 25 February 2018 ABSTRACT The Fe3O4 fluid synthesis by thermal decomposition method carried out in organic solvents with high boiling temperatures disposes a possibility of creating high-quality nanoparticles with uniform particle size and high degree of crystallization. In this paper, Fe 3O4 fluid was prepared by thermal decomposition using poly (maleic anhydride-alt-1-octadecene) (PMAO) as a phase transfer ligand. The crystalline structure, morphology and magnetic property of the as-prepared samples were thoroughly characterized. The results demonstrated that the magnetic Fe 3O4 nanomaterial was formed in liquid phase with spinel single phase structure, average size of 1316 nm, and high saturation magnetization (up to 70 emu/g). Iron oxide (Fe3O4) nanoparticles coated with biocompatible poly (maleic anhydride-alt-1-octadecene) (PMAO) were synthesized for use as an MRI (magnetic resonance imaging) contrast agent. The spin-lattice (T1) and the spin-spin (T2) relaxation times of the nuclear spins (hydrogen protons) in aqueous solutions of various concentrations of coated ferrite .

TỪ KHÓA LIÊN QUAN
crossorigin="anonymous">
Đã phát hiện trình chặn quảng cáo AdBlock
Trang web này phụ thuộc vào doanh thu từ số lần hiển thị quảng cáo để tồn tại. Vui lòng tắt trình chặn quảng cáo của bạn hoặc tạm dừng tính năng chặn quảng cáo cho trang web này.